90-7068-1407

Active

Kester Solder

SOLDER FLUX-CORED/48 .015" 100G

Search across all available documentation for this part.

Active

Kester Solder

SOLDER FLUX-CORED/48 .015" 100G

Technical Specifications

Parameters and characteristics for this part

Specification	90-7068-1407

Composition	Sn96.5Ag3Cu0.5 (96.5/3/0.5)
Diameter [diameter]	0.015 in
Diameter [diameter]	0.38 mm
Flux Type	Rosin Activated (RA)
Form	100 g
Form	Spool
Form	3.53 oz
Melting Point [Max]	218 °C
Melting Point [Max]	424 °F
Melting Point [Min]	217 °C
Melting Point [Min]	423 °F
Storage/Refrigeration Temperature [Max]	40 °C
Storage/Refrigeration Temperature [Min]	10 °C
Type	Wire Solder
Wire Gauge	27 AWG, 28 SWG

Part	Diameter [diameter]	Diameter [diameter]	Flux Type	Melting Point [Min]	Melting Point [Min]	Melting Point [Max]	Melting Point [Max]	Type	Storage/Refrigeration Temperature [Min]	Storage/Refrigeration Temperature [Max]	Wire Gauge	Form	Form	Form	Composition	Diameter [diameter]	Shelf Life Start	Shelf Life
Kester Solder 90-7068-1407	0.015 in	0.38 mm	Rosin Activated (RA)	217 °C	423 °F	218 °C	424 °F	Wire Solder	10 °C	40 °C	27 AWG 28 SWG	100 g	Spool	3.53 oz	Sn96.5Ag3Cu0.5 (96.5/3/0.5)
Kester Solder 90-7068-8850		0.01 in	No-Clean	217 °C	423 °F	218 °C	424 °F	Wire Solder	10 °C	40 °C	30 AWG 33 SWG	100 g	Spool	3.53 oz	Sn96.5Ag3Cu0.5 (96.5/3/0.5)	0.25 mm	Date of Manufacture	36 Months
Kester Solder 90-7068-6442		0.01 in	Water Soluble	217 °C	423 °F	218 °C	424 °F	Wire Solder	10 °C	40 °C	30 AWG 33 SWG	100 g	Spool	3.53 oz	Sn96.5Ag3Cu0.5 (96.5/3/0.5)	0.25 mm
Kester Solder 90-7068-6422	0.015 in	0.38 mm	Water Soluble	217 °C	423 °F	218 °C	424 °F	Wire Solder	10 °C	40 °C	27 AWG 28 SWG	100 g	Spool	3.53 oz	Sn96.5Ag3Cu0.5 (96.5/3/0.5)

Prices provided here are for design reference only. For realtime values and availability, please visit the distributors directly

Distributor	Package	Quantity	$

General part information

Lead Free Rosin Activated (RA) Wire Solder Sn96.5Ag3Cu0.5 (96.5/3/0.5) 27 AWG, 28 SWG Spool, 3.53 oz (100g)

Technical documentation and resources